Brazing Rod Copper 93,6% / Phospohrus 6% / Silver 0,4% - 1Kg
search
  • Brazing Rod Copper 93,6% / Phospohrus 6% / Silver 0,4% - 1Kg
  • Brazing Rod Copper 93,6% / Phospohrus 6% / Silver 0,4% - 1Kg

Brazing Rod Copper 93,6% / Phospohrus 6% / Silver 0,4% - 1Kg

€51.70
€31.92 Save 38.25%

(€31.92 articolo)

Brazing rod Copper 93,6% - Phosphorus 6% - Silver 0,4% high melting point alloy, ideal for brazing on copper pipes, with silver, perfect for capillary welding.

Quantity
In Stock

100% secure payments
  Security policy

(edit with the Customer Reassurance module)

  Delivery policy

(edit with the Customer Reassurance module)

  Return policy

(edit with the Customer Reassurance module)

Brazing rod for high melting point alloy, excellent for high resistance and standard brazing on copper pipes, with silver, perfect for capillary welding. Copper 93,6% / Phosphorus 6% /Silver 0,4% (1 Kg) in strips of 2 x 500 mm.

What we like about this brazing rod:

  • High melting point alloy, excellent for high resistance and standard brazing on copper pipes, with silver, perfect for capillary welding
  • Excellent for brazing copper pipes in sanitary and plumbing water systems and HVAC/R industry
  • Excellent for capillary brazing in copper pipes
  • Brazing rod size: 2x500 mm
  • Manufactured according to standards DIN EN 1044: 2001
  • Weight 1 Kg
  • Melting Point 700-850 °C
  • Mechanical Strength 450 N/mm²

How to use the solder Super 5:

  1. Ideal for welding Castolin
  2. Perform a flare in the copper pipe to be welded and clean it
  3. Insert the tube
  4. Heat the pipe with a MAP gas or oxy-acetylene torch up to the characteristic color "cherry red"
  5. Flow the filler metal alloy to the coupling until the space between the two tubes is filled
  6. Cool the tube
938041
20 Items

Data sheet

Weight (tool)
1,00 Kg
Tool size
2 x 500 mm
Standard equipment
Package 1 Kg
Lenght
500 mm
Made of
Copper 93,6% / Phosphorus 6% / Silver 0,4%
Melting point
700 - 850 °C
Mechanical strength
450 N/mm²